Paliocrom Gold L 2000
Pure Shade
chemical nature : aluminum flakes, coated with iron oxide
physical form : paste (65 % pigment,35 % white spirit)
physical data
density (20 °C [68 °F]): 1.50 g/cm³
specific surface: 3.50 m²/g
particle size distribution
D10 10 μm
D50 20 μm
D90 36 μm
resistance to chemicals (baking finish)
acids (HCl, 10 %) : 5
alkalis (NaOH, 10 %): 5
heat resistance: 200 °C
fastness to overcoating:
120 °C (248 °F), 30 min.: 5
150 °C (302 °F), 20 min. : 5
180 °C (356 °F), 10 min.: 5
hiding power (black-and-white contrast)
At a pigment weight concentration of 20 %, hidingis achieved at a dry film thickness of 10μm
fastness to weathering (Florida, 2 years, 2-coat metallic):
pure shade: 5
shelf life： at least 12 months from date of delivery if kept under dry conditions
and in unopened original containers
fields of application：
top-quality two-coat automotive, industrial and decorative finishes for novel effects in both
solvent- and water-based systems; suitable for powder coatings via bonding process。